Tamilselvi R, Kalaiarasi M, Elumalai M, Malarkodi T, Venkatesh A, Prakash V. Antimicrobial Activity of Metal Oxide Nanoparticles. Biomed Pharmacol J 2024;17(3).
Manuscript received on :01-06-2024
Manuscript accepted on :02-08-2024
Published online on: 01-10-2024
Plagiarism Check: Yes
Reviewed by: Dr. Sharad Kamble
Second Review by: Dr. Hanefi ÖZBEK
Final Approval by: Dr Jihan Seid Hussein

How to Cite    |   Publication History
Views Views: (Visited 138 times, 5 visits today)   Downloads PDF Downloads: 70

Ramachandran Tamilselvi1*, Maniarasu Kalaiarasi1, M. Elumalai2, Thanthoni Malarkodi3, Alagarswamy Venkatesh1, Venkatachalam Prakash1

1Department of Conservative Dentistry and Endodontics, Sree Balaji Dental College and Hospital, Bharath Institute of Higher Education and Research, Chennai, Tamilnadu, India.

2Department of Zoology and Biotechnology, Government Arts College, Nandanam, Chennai, Tamilnadu, India.

3Department of Oral Medicine and Radiology, Faculty of Dental Sciences, Sri Ramachandra Institute of Higher Education and Research, Chennai, Tamilnadu, India

Corresponding Author E-mail: drtamil_chandran@yahoo.co.in

DOI : https://dx.doi.org/10.13005/bpj/2981

Abstract

A broad range of gram positive and gram negative bacteria have been demonstrated to be effectively suppressed in growth by Metal Oxide Nanoparticles (MONPs), suggesting that these particles may be useful in the fight against antibiotic resistance. The antibacterial characteristics of MONPs, including those of silver, zinc, titanium, zirconia, iron, copper, magnesium, and cobalt oxide are widely recognized. The use of these nanoparticles made of synthetic and natural materials in dentistry is developing quickly, has been included in a variety of dental materials and has assisted in the treatment of oral disorders as well as the removal of biofilms and smear layers. The reader will gain up-to-date knowledge on MONPs, their modes of action, and their significance in endodontics in this review.

Keywords

Antibacterial; Drug delivery; Endodontic; Metal oxides; Multidrug resistant; Nanoparticles

Download this article as: 
Copy the following to cite this article:

Tamilselvi R, Kalaiarasi M, Elumalai M, Malarkodi T, Venkatesh A, Prakash V. Antimicrobial Activity of Metal Oxide Nanoparticles. Biomed Pharmacol J 2024;17(3).

Copy the following to cite this URL:

Tamilselvi R, Kalaiarasi M, Elumalai M, Malarkodi T, Venkatesh A, Prakash V. Antimicrobial Activity of Metal Oxide Nanoparticles. Biomed Pharmacol J 2024;17(3). Available from: https://bit.ly/3ZLBI2r

Introduction

Human body biology is associated with a variety of microbial symbionts and their genomes. The microbial population rapidly colonizes both the inside and outside of our bodies, developing an organ that is essential to our physiology and general health. There are about 1000 different types of bacteria in the mouth, making the populations incredibly complicated. They are second in complexity in the body, after the colon, according to estimates1. One of the body’s most varied micro biomes is in the human mouth2. Viruses, protozoa, archaea, fungus, and bacteria make up the oral microbiome3.

With an elevated risk of infection during various operations, the oral cavity is the home to a multitude of bacteria which is significant in the dental profession. Normal microflora typically comprises of a modest number of mutans microorganisms (most notably Streptococcus mutans and Streptococcus sobrinus) and non-mutans streptococci (such as Streptococcus salivarius, Streptococcus sanguis, etc.). Any disruption to the microbial ecosystem could make it easier for more pathogenic microbes to enter the environment, including Escherichia coli, S. aureus, Aggregatibacter actinomycetemcomitans, Porphyromonas gingivalis, and others4.

A significant worldwide problem is the rise in bacterial resistance to one or more antibiotics5 . Newly, Nanomaterials have emerged as a weapon against bacteria resistant to many drugs. These nanoparticles can be employed as nanomedicines to combat resistant bacteria by working alone or in concert with other antibacterial substances. In order to improve physical and chemical characteristics and therapeutic efficacy, nanomaterials are often employed as drug delivery vehicles. A highly researched class of nanomaterials against bacteria resistant to many drugs are metal and MONPs. Metals such as gold, silver, titanium, copper, zinc and aluminum as well as metal oxides including silver, copper, magnesium, calcium and zinc oxide can be used to create these nanoparticles6.

Materials with unique features at the nano scale, or between 1 and 100 nanometers, gave rise to the field of nanotechnology, which was first described by Norio Taniguchi in 1974 and began to take shape in the 1980s. The incorporation of nanoscale features into material components including those intended for dental use is made possible by nanotechnology7. Innovative methods in dentistry make use of nanoparticles that have therapeutic properties on their own or employ nanotechnology to improve the results of current treatments8. The primary advantages of nanomaterials in dentistry are their efficient and broad antibacterial properties, which come with a low cost of production for the nanoparticles and a minimal chance of bacterial resistance developing9. The current article aims to provide an overview of the antibacterial properties of metal oxide-containing nanoparticles used in dentistry.

Microbiology of Root canal Infections

Aerobes and facultative anaerobes initially predominate in the bacterial ecology of the root canal10,11 The ecology of the root canal system changes as the condition worsens. These alterations may be connected to the oxygen tension during root canal openings for therapeutic purposes, the application of root canal irrigants, and pH variations in the root canal as a result of different materials being inserted. Due to genetic population shifts, this leads to phenotypic changes12,13,14. An endodontic infection may be primary or secondary. Apical periodontitis, or inflammation of the supporting tissues, is the ultimate result of microbial byproducts or microbial invasion, which typically causes pulp inflammation and root canal infection as its primary infection. Infections that return in teeth after root canal therapy can be classified as secondary infections, post-treatment infections, emergent or acquired reinfections, or persistent residual infections15. Polymicrobial infections cause primary endodontic infections14,16. The most common species among them include Eubacterium, Camphylobacter, Fusobacterium, Treponema, Prophyromonas, Prevotella, and Bacteroides.

Treatment failure is thought to be mostly caused by bacteria that continue to exist in the root canal system after treatment17,18,19. After root canal therapy, the diversity and number of bacterial species in primary infections can change, as well as the proportions of different bacteria. Microbial flora in secondary infections often adapt to harsh conditions such as broad pH ranges and nutrient-limited environments. The microbial phenotypes of primary infections and subsequent infections differ significantly, with gram-positive bacteria predominating in the latter18,19,20.  Research has indicated that specific species, including Enterococci, Streptococci, Lactobacilli, Actinomyces, and fungus (like Candida), are more common in teeth that have had post-treatment infections. Specifically, it was found that a significant percentage of Enterococcus faecalis was present in patients with persistent apical periodontitis21,22.

Mechanism of Action of Metal Oxide (MO) Nanoparticles

Breakdown of the Cell Membrane Caused by Electrostatic Interaction

The negatively charged surfaces of bacteria interact with positively charged nanoparticles through the law of attraction between negative and positive charges, causing NPs to accumulate on the surface of bacterial cells. Because of the efficient bonding between these positively charged NPs and the cell membrane, the structure of the cell wall is disrupted, which makes the cell more permeable and makes it easier for NPs to enter the bacteria and cause cellular content escape. Those nanoparticles impact DNA replication, division, and respiration by attaching to mesosomes23,24.

Generation of Reactive Oxygen Species (ROS)

When nanoparticles penetrate a microorganism’s cell membrane, they release ROS, which puts the cell under stress due to oxidation and initiates the bacterium’s attack. The attack results in reduced respiration and ATP synthesis, which damages the cell membrane. Active redox reactions and the pro-oxidant functional group on the metal oxide nanoparticles interface allow a metal oxide to produce ROS25.

Enzyme and Protein Malfunction

By initiating the oxidative process of the amino acid chain, NPs promote the creation of carbonyls, which are naturally protein bound and result in protein breakdown, the deactivation of numerous enzymes, and disruption of catalytic activity26,27.

Genotoxicity and Inhibition of Signal Transduction

Through their electrical properties, nanoparticles interact with amino acid molecules, impairing signal transduction and negatively affecting chromosomal and plasmid transcription processes28,29,30.

Effective Physiochemical Properties of MONPs on Antimicrobial Activity

Chemical Composition of MONPs

The antibacterial ability of metal oxides is impacted by the kind of metal ion particles and the composition of their molecules. Metal ions including Ca2+, Mg2+, Cu2+, Zn2+, Co2+, Fe2+, and Ni2+ are required for various metabolic processes in the majority of surviving bacterial strains, but at larger quantities, they may be toxic. Ag+ and Hg+, two unnecessary metal ions, demonstrated a significantly higher antibacterial action at remarkably low quantities31. The ability of metal ions to bind selectively to ligand atoms found in biomolecules and cellular constituents may contribute to their antibacterial action. Hard soft acid base theory is the foundation for the interaction between ligand atoms and metal ions (HSAB principle). According to the HSAB principle, hard acids join with hard bases, while soft acids join with soft bases32.  An excellent affinity of divalent copper for biological molecules is shown by the Irving Williams series of ligand affinity for the essential first-row transition divalent metal ions. This shows that at higher concentrations, divalent copper may be most dangerous33.

MONPs Size and Surface Properties

Particle size has a major impact on how MONPs interact with bacterial cells and other biological systems. Because of their increased surface to volume ratios and noticeably higher particle numbers per mass, nanoparticles demonstrated stronger antibacterial activity than microscaled (bulk) particles. Numerous reports have documented the size-dependent interaction between bacteria and MO nanostructures. Under normal lighting conditions, the Zinc Oxide Nanoparticles (ZnONPs) considerably inhibit gram-positive as well as gram-negative bacteria in comparison to the bulk particles34,35,36. The zeta potential of MONPs describes their surface charge characteristics. The Point of Zero Charge (PZC) is the pH at which the surface charge is neutral. MONPs can exhibit positive, negative, or neutral charges. NPs with the highest positive charge show the greatest antibacterial activity, followed by those with neutral, then negative charges. When the pH is below the PZC, the oxide surface is positively charged; when above, it is negatively charged.

Concentration of MONPs:

With increasing concentration in the media, MONPs exhibit increased antibacterial activity37. Greater MONP concentrations may be associated with a greater surface area, this eventually promotes stronger contact with bacterial cells and increased antibacterial activity. The Minimum Inhibitory Concentration (MIC) is the most often used metric in microbiology to quantify the in vitro antibacterial activity assessment of MONP38. The MIC of an antimicrobial drug is the concentration at which, following overnight incubation, bacteria cannot grow visibly39.

The shape dependent antibacterial characteristics of MONPs:

Each form of nanoparticle has unique physicochemical properties, such as surface characteristics, solubility, and the potential to produce ROS in certain metal oxides, which influence their antibacterial activity. Studies show that different forms of MO-NPs exhibit varying antibacterial properties. For instance, ZnO nanopyramids have significantly greater antibacterial activity against Methicillin-Resistant Staphylococcus aureus (MRSA) compared to nanoplates and nanospheres40. Another study found that spherical ZnO NPs possess higher antibacterial power than rod-shaped ZnO NPs34.

 Various MONPs in Endodontics:

 Iron Oxide (IO NP)

The biological and medical fields find application for iron compound (FeO2) nanoparticles. Iron oxide, a sustainable and biocompatible material that can be made on a big scale at a low cost by simple chemical synthesis techniques, is now included in FDA-approved formulations for chronic treatment.

Despite the fact the NaOCl is considered the “gold standard” for endodontic irrigants41, it have been observed that 40% to 60% of root canals still contain live bacteria even after irrigation42. Similar antibacterial activity to NaOCl has also been demonstrated for chlorhexidine43. But only the surface layers of the dentin exhibit antibacterial activity and both irrigants have shown decreased efficiency in disinfecting dentinal tubules44. IO NP/H2O2 had strong antibacterial activity that was notably superior to chlorhexidine and sodium hypochloride in the treatment of dentinal tubule infections caused by E. faecalis, especially in the central and peripheral zones. Because of IO NP’s innate “peroxidase-like activity,” which activates H2O2, a high degree of disinfection can be made possible, which catalyses the production of free radicals on the spot, which quickly destroys bacteria45.

Silver Oxide

The most extensively studied antibacterial for endodontic infections is silver nanoparticles. While retaining the physicochemical characteristics of the produced sealers, it was discovered that adding 10 weight percent Ag with SiO2 decreased the viability of E. faecalis during both immediate and longitudinal study46. It was discovered to help regulate the growth of bacteria in the intracanal environment and to be just as effective against E. faecalis and Staphylococcus aureus as 5.25% NaOCl47. Nevertheless, extended exposure to bacteria is necessary for their successful eradication, which has been described as a good substitute for an intracanal medication but not as an irrigant48.

Copper Oxide

Copper is a cheap, readily available metal that can be affordably manufactured into nanoparticles. Either copper metal ions or oxidized cupric ions produced from copper nanoparticles (sizes ranging from 1 to 100 nm) have antimicrobial action. It is simple to mix and link copper nanoparticles with polymers, ceramics and other metals. In certain combinations, they exhibit physiochemical stability as well49. Copper is a common metal in dental and medical research because of its low toxicity and antibacterial properties50. According to reports, Copper Oxide Nanoparticles (CuO NPs) exhibit antibacterial properties and prevent the formation of biofilms51. Copper nanoparticles’ high surface area to volume ratio amplifies their antibacterial activity52. Furthermore, dose dependence is shown in the antibacterial activity of copper oxide nanoparticles53. The antibacterial properties of these nanoparticles have been well studied, yet it is unclear how precisely copper nanoparticles work against microorganisms54,55,56. These nanoparticles are effective against both gram positive and gram negative bacteria because they have the ability to enter bacterial cell membranes and damage the organism’s vital enzymes. They possess some antifungal properties as well57.

In caries prevention, copper nanoparticles have the ability to inhibit S. mutans from growing and colonizing on the surface of tooth roots, hence preventing root caries58. Composites with distinct physio chemical properties can be created by simply incorporating copper oxide nanoparticles into polymers. Copper oxide nanoparticles can be used to dental adhesive to prevent early or carious white spot lesions because they are antibacterial without compromising shear bond strength59,60. In soft denture liners CuO NPs were added, and this resulted in a considerable reduction in oral pathogen colonization and plaque development, particularly C. albicans accumulation61.

Zirconium Oxide

Because of its metallic and optical characteristics that are comparable to those of teeth, zirconia has found extensive application in dentistry. Zirconium oxide (ZrO2) has been known as a high-performance ceramic material due to its superior properties, high strength, resistance to corrosion, and toughness. Because of its insolubility in water, it has been demonstrated to eliminate bacterial colonization with little cytotoxic effects62,63. Because zirconia-based NPs are so effective against some infections like E. faecalis, they are commonly used as a type of antimicrobial in endodontics64.  The most used agent for pulp capping, whether direct or indirect, and root end filing is mineral trioxide aggregate (MTA). Portland cement is the main ingredient in MTA. Zirconia nanoparticles (NPs) can be added to Portland cement as an effective radio opacifier without having a detrimental effect on the cement’s biocompatibility. According to ISO/ADA guidelines, both groups of micro- and nano-sized zirconia oxide particles showed improved radiopacity capabilities when examined63. In caries-affected dentine, an investigation on aluminum zirconate nanoparticles in etch and rinse adhesive revealed that 10 weight percent of the nanoparticles in the adhesive had the lowest survival rate of S. mutans65.

Titanium dioxide

Very stable particles with photocatalytic properties are titanium dioxide nanoparticles. Because ROS are produced, it results in oxidative stress. Because of its lipid peroxidation property, the cell membrane is disrupted and there is increased membrane fluidity even for the types of fungus that are resistant to fluconazole, it is also a potent antifungal5,66,67.  Because of its excellent aesthetics and simplicity of use, Dental resin composite is a useful restoration technique for teeth that have decayed68,69,70, its perfect finishing and enhanced resistance to wear make it an excellent choice. However, it should be mentioned that in the case of a long-term dental resin repair, the bacteria will persist in growing and forming oral biofilms on the surface of the resin, particularly in the gap that are polymerization shrinkage produced. These biofilms will then continuously deteriorate the surrounding dental tissue and the current resin composite, leading to secondary caries and treatment failure71,72.  Photo catalytic activity of synthesized anatase-phase Strontium Nitrogen Titanium dioxide (Sr, N, TiO2) was increased by mixing  with Nano Hydroxyapatite (nHA) fillers as reinforcing fillers to create a novel multifunctional Direct Resin Composite. It possesses antimicrobial and mineralizing properties because Sr, N, TiO2 and nHA combine. The mutans strain of Streptococcus (S. mutans) was the target of the maximum antibacterial rate of 98.96%, which helped the resin composite survive longer in the clinical environment. Consequently, they conclude that the Direct resin composite in conjunction with nHA & Sr, N, TiO2 fillers will probably be the most effective filler for filling dental cavities73.

Zinc Oxide

Although most living things require zinc as a trace metal for numerous metabolic functions, excessive amounts of zinc can be toxic. Because ZnO NPs are less harmful to humans than CuO NPs and AgO NPs and can be synthesized at a cheap cost, they are frequently utilized in cosmetic items, medicine and wound healing to treat fungal infections and acne. They also display a broad spectrum of antibacterial activity74.It has been discovered that ZnO NPs possess antibacterial qualities. Modest amounts of ZnO NPs had no effect on the mechanical properties of dental resin composites, but they did prevent S. mutans from growing and adhering to the material75. When ZnO NPs were added into Glass Ionomer Cement, it considerably increase antibacterial activities against S. mutans without affecting mechanical properties76. According to the study, ZnO NP doped with magnesium and silver has a stronger antibacterial effect than ZnO NP against S. mutans. Synthesized NP exhibits antibacterial activity against bacteria when its cell walls are compromised. These results in the distortion of constructional proteins, inactivation of enzymes, disruption of electron transport chains, deformation of nucleic acids, and facilitation of oxidative stress caused by reactive oxygen species. According to a number of studies, adding ZnO NPs to dental adhesive systems greatly enhanced their antimicrobial capabilities without having a negative impact on the bond strength77,78,79.

One method that is most frequently utilized to treat endodontic infections is endodontic treatment80,81. Complete eradication of dental infections is not possible because to the polymicrobial character of endodontic infections, which involve a variety of bacteria and germs such as E. faecalis, S. mutans and S. anginosus, F. nucleatum, and S. aureus82,83.  An excellent filling material for root canals should not shrink, fill the channels easily, stick to the walls easily, or harm the periapical tissue or permanent tooth germ. Additionally, two important considerations while selecting the best among them are their antibacterial and biocompatible qualities84,85.  The micro leakage and antibacterial properties of zinc oxide eugenol (ZOE), epoxy resin sealer (AH26), silver ZnO nano powders, and ZnO nanopowders were investigated. Shayani Rad reports that the nano ZnO sealer demonstrated better antibacterial properties against E. faecalis, E. coli, C. albicans, S. mutans, and S. aureus than two widely used endodontic sealers, AH26 (resin-based) and Pulpdent (ZnO based)86,87.  These nanoparticles enhance alkalinization and antibacterial activity against Escherichia faecalis when coupled with calcium hydroxide nanoparticles and chlorhexidine as an intracanal medication. After being coated with ZnO NPs and pre-treated with argon plasma, flawless gutta percha cones displayed antibacterial action against S. aureus and E. faecalis. As a result, there is less chance of reinfection and endodontic failure and an effective hermetic seal is created88. Calcium silicate cement containing 1 wt% ZnO NPs can decrease pro-inflammatory cytokines and increase antibacterial activity without  altering its physical characteristics89.

 Magnesium oxide

The caries process includes demineralization of hydroxyapatite due to acid attack90,91. Alkaline nanoparticles could therefore be a substitute for preventing dental cavities. About 0.5% of enamel and 1% of dentine are made of the alkaline metal magnesium92,93.  According to a study, having enough serum magnesium levels can slow down the onset and development of tooth caries by releasing magnesium ions94.  Glass ionomer cement treated with magnesium oxide nanoparticles exhibited strong antibacterial and biofilm activity against cariogenic bacteria95. Limited studies reported the use of magnesium nanoparticles to prevent dental cavities. Tooth decay and magnesium exhibit both substantial94 and nonsignificant relationships96. According to the study, ZnO NP doped with magnesium and silver has a stronger antibacterial effect than ZnO NP against S. mutans. Synthesized NP exhibits antibacterial activity against bacteria when its cell walls are compromised. This results in the distortion of constructional proteins, inactivation of enzymes, disruption of electron transport chains, deformation of nucleic acids, and facilitation of oxidative stress caused by reactive oxygen species97,98.

Cobalt oxide

One of the transition metal oxides, cobalt oxide (CO), is a black powder having magnetic and antibacterial properties99. They were added to Pit and Fissure Sealant (PFS) in order to address important clinical issues related with PFS, including microleakage and secondary caries. An investigation on antibacterial potential of Minocycline (MNC) with CO, a pH-dependent cobalt oxide nanoparticle integrated with MNC, by characterizing and testing it against Streptococcus sobrinus. They discovered that 2.5% MNC with CO doped PFS demonstrated strong anti-biofilm capabilities without sacrificing mechanical characteristics100.

Conclusion

Due to their excellent mechanical, chemical, biological, and physical properties, nanomaterials (NMs) have recently become more and more prominent in technological advancements. These qualities have allowed performance to rise above that of its conventional counterparts. Nanomaterials can be used to fight endodontic and caries-related bacteria, lessen the formation of biofilms, and prevent the demineralization of the tooth structure. These results have been positive enough to open the door for more clinical studies that will confirm the usefulness of nanotechnology-based materials for therapeutic purposes. Thus, by promoting better oral health and lowering healthcare costs, the use of metal oxide nanoparticles in dentistry can ultimately benefit both individual patients and society at large. It can also increase the antibacterial efficacy, lengthen the duration of dental treatments and significantly reduce the incidence of dental diseases.

Acknowledgement

The authors appreciate and thank Sree Balaji Dental College, Bharath Institute of Higher Education and Research for supporting this research publication.

Conflict of Interest

The author(s) declares no conflict of interest.

Funding Source

The author(s) received no financial support for the research, authorship, and/or publication of this article.

Data Availability Statement

This statement does not apply to this article.

Ethics Statement

This research did not involve human participants, animal subjects, or any material that requires ethical approval.

References

  1. Belibasakis GN. Microbiological changes of the ageing oral cavity. Arch Oral Biol., 2018;96:230-232.
  2. Yamashita Y, Takeshita T. The oral microbiome and human health. J Oral Sci., 2017;59(2):201-206.
  3. Wade WG. The oral microbiome in health and disease. Pharmacol Res., 2013;69(1):137-143.
  4. Patil S, Rao RS, Sanketh DS, Amrutha N. Microbial flora in oral diseases. J Contemp Dent Pract., 2013;14(6):1202-1208.
  5. Allahverdiyev AM, Abamor ES, Bagirova M, Rafailovich M. Antimicrobial effects of TiO2 and Ag2O nanoparticles against drug-resistant bacteria and leishmania parasites. Future Microbiol., 2011;6(8):933-940.
  6. Niño-Martínez N, Salas Orozco MF, Martínez-Castañón GA, Torres Méndez F, Ruiz F. Molecular mechanisms of bacterial resistance to metal and metal oxide nanoparticles. Int J Mol Sci., 2019;20(11):2808.
  7. Yao C, Storey D, Webster TJ. Nanostructured metal coatings on polymers increase osteoblast attachment. Int J Nanomedicine., 2007;2(3):487-492.
  8. Padovani GC, Feitosa VP, Sauro S, et al. Advances in dental materials through nanotechnology: facts, perspectives and toxicological aspects. Trends Biotechnol., 2015;33(11):621-636.
  9. Hamouda IM. Current perspectives of nanoparticles in medical and dental biomaterials. J Biomed Res., 2012;26(3):143-151.
  10. Winkler KC, Van Amerongen J. Bacteriologic results from 4,000 root canal cultures. Oral Surg Oral Med Oral Pathol., 1959;12(7):857-875.
  11. Antunes HS, Rôças IN, Alves FRF, Siqueira JF. Total and specific bacterial levels in the apical root canal system of teeth with post-treatment apical periodontitis. J Endod., 2015;41(7):1037-1042.
  12. Byström A, Sundqvist G. Bacteriologic evaluation of the efficacy of mechanical root canal instrumentation in endodontic therapy. Scand J Dent Res., 1981;89(4):321-328.
  13. Sundqvist GK, Eckerbom MI, Larsson AP, Sjögren UT. Capacity of anaerobic bacteria from necrotic dental pulps to induce purulent infections. Infect Immun., 1979;25(2):685-693.
  14. Provenzano JC, Siqueira JF, Rôças IN, et al. Metaproteome analysis of endodontic infections in association with different clinical conditions. PLoS One., 2013;8(10).
  15. Haapasalo M, Udnæs T, Endal U. Persistent, recurrent, and acquired infection of the root canal system post-treatment. Endod Topics., 2003;6(1):29-56.
  16. Rôças IN, Siqueira JF. Identification of bacteria enduring endodontic treatment procedures by a combined reverse transcriptase-polymerase chain reaction and reverse-capture checkerboard approach. J Endod., 2010;36(1):45-52.
  17. Alves FRF, Andrade-Junior CV, Marceliano-Alves MF, et al. Adjunctive steps for disinfection of the mandibular molar root canal system: a correlative bacteriologic, micro-computed tomography, and cryopulverization approach. J Endod., 2016;42(11):1667-1672.
  18. Anderson AC, Hellwig E, Vespermann R, et al. Comprehensive analysis of secondary dental root canal infections: a combination of culture and culture-independent approaches reveals new insights. PLoS One., 2012;7(11):e49576.
  19. Lins RX, de Oliveira Andrade A, Hirata Junior R, et al. Antimicrobial resistance and virulence traits of Enterococcus faecalis from primary endodontic infections. J Dent., 2013;41(9):779-786.
  20. Ran S, He Z, Liang J. Survival of Enterococcus faecalis during alkaline stress: changes in morphology, ultrastructure, physiochemical properties of the cell wall and specific gene transcripts. Arch Oral Biol., 2013;58(11):1667-1676.
  21. Love RM. Enterococcus faecalis—a mechanism for its role in endodontic failure. Int Endod J., 2001;34(5):399-405.
  22. Wang J, Jiang Y, Chen W, Zhu C, Liang J. Bacterial flora and extraradicular biofilm associated with the apical segment of teeth with post-treatment apical periodontitis. J Endod., 2012;38(7):954-959.
  23. Kim YH, Lee DK, Cha HG, et al. Preparation and characterization of the antibacterial Cu nanoparticle formed on the surface of SiO2 nanoparticles. J Phys Chem., 2006;110(49):24923-24928.
  24. Wang D, Lin Z, Wang T, et al. Where does the toxicity of metal oxide nanoparticles come from: the nanoparticles, the ions, or a combination of both? J Hazard Mater., 2016;308:328-334.
  25. Nel A, Xia T, Mädler L, Li N. Toxic potential of materials at the nanolevel. Science., 2006;311(5761):622-627.
  26. Lynch I, Salvati A, Dawson KA. Protein-nanoparticle interactions: what does the cell see? Nat Nanotechnol., 2009;4(9):546-547.
  27. Aggarwal P, Hall JB, McLeland CB, Dobrovolskaia MA, McNeil SE. Nanoparticle interaction with plasma proteins as it relates to particle biodistribution, biocompatibility and therapeutic efficacy. Adv Drug Deliv Rev., 2009;61(6):428-437.
  28. Giannousi K, Lafazanis K, Arvanitidis J, Pantazaki A, Dendrinou-Samara C. Hydrothermal synthesis of copper-based nanoparticles: antimicrobial screening and interaction with DNA. J Inorg Biochem., 2014;133:24-32.
  29. Arakha M, Pal S, Samantarrai D, et al. Antimicrobial activity of iron oxide nanoparticle upon modulation of nanoparticle-bacteria interface. Sci Rep., 2015;5:14813.
  30. Kirstein J, Turgay K. A new tyrosine phosphorylation mechanism involved in signal transduction in Bacillus subtilis. J Mol Microbiol Biotechnol., 2005;9(3-4):182-188.
  31. Lemire JA, Harrison JJ, Turner RJ. Antimicrobial activity of metals: mechanisms, molecular targets and applications. Nat Rev Microbiol., 2013;11(6):371-384.
  32. Pearson RG. Hard and soft acids and bases. J Am Chem Soc., 1963;85(22):3533-3539.
  33. Miličević A, Branica G, Raos N. Irving-Williams order in the framework of connectivity index 3χv enables simultaneous prediction of stability constants of bivalent transition metal complexes. Molecules., 2011;16(2):1103-1112.
  34. Nair S, Sasidharan A, Divya Rani VV, Menon D, Nair S, Manzoor K, Raina S. Role of size scale of ZnO nanoparticles and microparticles on toxicity toward bacteria and osteoblast cancer cells. J Mater Sci Mater Med., 2009;20:235-41.
  35. Raghupathi KR, Koodali RT, Manna AC. Size-dependent bacterial growth inhibition and mechanism of antibacterial activity of zinc oxide nanoparticles. Langmuir., 2011;27(7):4020-4028.
  36. Jones N, Ray B, Ranjit KT, Manna AC. Antibacterial activity of ZnO nanoparticle suspensions on a broad spectrum of microorganisms. FEMS Microbiol Lett., 2008;279(1):71-76.
  37. Pandiyarajan T, Udayabhaskar R, Vignesh S, James RA, Karthikeyan B. Synthesis and concentration dependent antibacterial activities of CuO nanoflakes. Mater Sci Eng C Mater Biol Appl., 2013;33(4):2020-2024.
  38. Dimapilis EA, Hsu CS, Mendoza RM, Lu MC. Zinc oxide nanoparticles for water disinfection. Sustain Environ Res., 2018;28(2):47-56.
  39. Andrews JM. Determination of minimum inhibitory concentrations. J Antimicrob Chemother., 2001;48 Suppl 1:5-16.
  40. Cha SH, Hong J, McGuffie M, Yeom B, VanEpps JS, Kotov NA. Shape-dependent biomimetic inhibition of enzyme by nanoparticles and their antibacterial activity. ACS Nano., 2015;9(9):9097-9105.
  41. Bukhari S, Kim D, Liu Y, Karabucak B, Koo H. Novel endodontic disinfection approach using catalytic nanoparticles. J Endod., 2018;44(5):806.
  42. Byström A, Sundqvist G. The antibacterial action of sodium hypochlorite and EDTA in 60 cases of endodontic therapy. Int Endod J., 1985;18(1):35-40.
  43. Lopes MB, Sinhoreti MA, Gonini Júnior A, Consani S, McCabe JF. Comparative study of tubular diameter and quantity for human and bovine dentin at different depths. Braz Dent J., 2009;20(4):279-283.
  44. Heling I, Chandler NP. Antimicrobial effect of irrigant combinations within dentinal tubules. Int Endod J., 1998;31(1):8-14.
  45. Gao L, Liu Y, Kim D, et al. Nanocatalysts promote Streptococcus mutans biofilm matrix degradation and enhance bacterial killing to suppress dental caries in vivo. Biomaterials., 2016;101:272-284.
  46. Rücker VB, Balbinot GS, Collares FM, de Araújo Neto VG, Giannini M, Leitune VCB. Synthesis of silver core-shell nanoparticles and their influence on an experimental resin endodontic sealer: an in vitro analysis. Int Endod J., 2023;56(2):289-303.
  47. Moghadas L, Shahmoradi M, Narimani T. Antimicrobial activity of a new nanobased endodontic irrigation solution: in vitro study. Dent Hypotheses., 2012;3:142.
  48. Wu D, Fan W, Kishen A, Gutmann JL, Fan B. Evaluation of the antibacterial efficacy of silver nanoparticles against Enterococcus faecalis biofilm. J Endod., 2014;40(2):285-290.
  49. Xu VW, Nizami MZI, Yin IX, et al. Application of copper nanoparticles in dentistry. Nanomaterials (Basel)., 2022;12(5):805.
  50. Chandraleka S, Ramya K, Chandramohan G, et al. Antimicrobial mechanism of copper (II) 1,10-phenanthroline and 2,2′-bipyridyl complex on bacterial and fungal pathogens. J Saudi Chem Soc., 2014;18(6):953-962.
  51. Maleki Dizaj S, Barzegar-Jalali M, Zarrintan MH, Adibkia K, Lotfipour F. Calcium carbonate nanoparticles as cancer drug delivery system. Expert Opin Drug Deliv., 2015;12(10):1649-1660.
  52. Soltani Nezhad S, Rabbani Khorasgani M, Emtiazi G, Yaghoobi MM, Shakeri S. Isolation of copper oxide (CuO) nanoparticles resistant Pseudomonas strains from soil and investigation on possible mechanism for resistance. World J Microbiol Biotechnol., 2014;30(3):809-817.
  53. Chang YN, Zhang M, Xia L, Zhang J, Xing G. The toxic effects and mechanisms of CuO and ZnO nanoparticles. Materials (Basel)., 2012;5(12):2850-2871.
  54. Chatterjee AK, Sarkar RK, Chattopadhyay AP, et al. A simple robust method for synthesis of metallic copper nanoparticles of high antibacterial potency against E. coli. Nanotechnology., 2012;23(8):085103.
  55. Essa AM, Khallaf MK. Antimicrobial potential of consolidation polymers loaded with biological copper nanoparticles. BMC Microbiol., 2016;16(1):144.
  56. Zakharova OV, Godymchuk AY, Gusev AA, et al. Considerable variation of antibacterial activity of Cu nanoparticles suspensions depending on the storage time, dispersive medium, and particle sizes. Biomed Res Int., 2015;2015.
  57. Ahamed M, Alhadlaq HA, Khan MAM, Karuppiah P, Al-Dhabi NA. Synthesis, Characterization, and Antimicrobial Activity of Copper Oxide Nanoparticles. J Nanomater., 2014;2014.
  58. Thneibat A, Fontana M, Cochran MA, Gonzalez-Cabezas C, Moore BK, Matis BA, et al. Anticariogenic and antibacterial properties of a copper varnish using an in vitro microbial caries model. Oper Dent., 2008;33(2):142–8.
  59. Toodehzaeim MH, Zandi H, Meshkani H, Hosseinzadeh Firouzabadi A. The Effect of CuO Nanoparticles on Antimicrobial Effects and Shear Bond Strength of Orthodontic Adhesives. J Dent (Shiraz)., 2018;19(1):1–5.
  60. Gutiérrez MF, Malaquias P, Matos TP, Szesz A, Souza S, Bermudez J, et al. Mechanical and microbiological properties and drug release modeling of an etch-and-rinse adhesive containing copper nanoparticles. Dent Mater., 2017;33(3):309–20.
  61. Ansarifard E, Zareshahrabadi Z, Sarafraz N, Zomorodian K. Evaluation of Antimicrobial and Antibiofilm Activities of Copper Oxide Nanoparticles within Soft Denture Liners against Oral Pathogens. Bioinorg Chem Appl., 2021;2021:9939275.
  62. Lughi V, Sergo V. Low temperature degradation -aging- of zirconia: A critical review of the relevant aspects in dentistry. Dent Mater., 2010;26(8):807–20.
  63. Bona AD, Pecho OE, Alessandretti R. Zirconia as a Dental Biomaterial. Materials (Basel)., 2015;8(8):4978-4991.
  64. Guerreiro-Tanomaru JM, Trindade-Junior A, Cesar Costa B, da Silva GF, Drullis Cifali L, Basso Bernardi MI, et al. Effect of Zirconium Oxide and Zinc Oxide Nanoparticles on Physicochemical Properties and Antibiofilm Activity of a Calcium Silicate-Based Material. ScientificWorldJournal. 2014;2014:975213.
  65. Niazi FH, Luddin N, Alghawazi AM, Al Sebai L, Alqerban A, Alqahtani YM, Barakat A, Samran A, Noushad M. Aluminum zirconate nanoparticles in etch and rinse adhesive to caries affected dentine: An in-vitro scanning electron microscopy, elemental distribution, antibacterial, degree of conversion and micro-tensile bond strength assessment. Microsc Res Tech., 2024;87(8):1955-1964.
  66. Mohammadi S, Mohammadi P, Hosseinkhani S, Shipour R. Antifungal Activity of TiO2 nanoparticles and EDTA on Candida albicans Biofilms. Infect Epidemiol Med., 2013;1:33–8.
  67. Ahmed FY, Farghaly Aly U, Abd El-Baky RM, Waly NGFM. Comparative Study of Antibacterial Effects of Titanium Dioxide Nanoparticles Alone and in Combination with Antibiotics on MDR Pseudomonas aeruginosa Strains. Int J Nanomedicine., 2020;15:3393–404.
  68. Zhang JF, Wu R, Fan Y, Liao S, Wang Y, Wen ZT, et al. Antibacterial dental composites with chlorhexidine and mesoporous silica. J Dent Res., 2014;93(12):1283–9.
  69. Xue J, Wang J, Feng D, Huang H, Wang M. Application of Antimicrobial Polymers in the Development of Dental Resin Composite. Molecules., 2020;25(20):4738.
  70. Sun Y, Zhou Z, Jiang H, Duan Y, Li J, Liu X, et al. Preparation and evaluation of novel bio-based Bis-GMA-free dental composites with low estrogenic activity. Dent Mater., 2022;38(2):281–93.
  71. Askar H, Krois J, Göstemeyer G, Schwendicke F. Secondary caries risk of different adhesive strategies and restorative materials in permanent teeth: Systematic review and network meta-analysis. J Dent., 2021;104:103541.
  72. Beck F, Lettner S, Graf A, Bitriol B, Dumitrescu N, Bauer P, et al. Survival of direct resin restorations in posterior teeth within a 19-year period (1996-2015): A meta-analysis of prospective studies. Dent Mater., 2015;31(8):958–85.
  73. Montoya C, Jain A, Londoño JJ, Correa S, Lelkes PI, Melo MA, et al. Multifunctional Dental Composite with Piezoelectric Nanofillers for Combined Antibacterial and Mineralization Effects. ACS Appl Mater Interfaces., 2021;13(37):43868–79.
  74. Moezzi A, McDonagh AM, Cortie MB. Zinc oxide particles: Synthesis, properties and applications. Chem Eng J., 2012;185–186:1–22.
  75. Wang Y, Hua H, Li W, Wang R, Jiang X, Zhu M. Strong antibacterial dental resin composites containing cellulose nanocrystal/zinc oxide nanohybrids. J Dent., 2019;80:23–9.
  76. Vanajassun PP, Nivedhitha MS, Nishad NT, Soman D. Effects of Zinc Oxide Nanoparticles in Combination with Conventional Glass Ionomer Cement: In vitro Study. Adv Hum Biol., 2014;4(3):31.
  77. Saffarpour M, Rahmani M, Tahriri M, Peymani A. Antimicrobial and bond strength properties of a dental adhesive containing zinc oxide nanoparticles. Braz J Oral Sci., 2016;15(1):66–9.
  78. Jowkar Z, Farpour N, Koohpeima F, Mokhtari MJ, Shafiei F. Effect of Silver Nanoparticles, Zinc Oxide Nanoparticles and Titanium Dioxide Nanoparticles on Microshear Bond Strength to Enamel and Dentin. J Contemp Dent Pract., 2018;19(11):1404–11.
  79. Gutiérrez MF, Alegría-Acevedo LF, Méndez-Bauer L, Bermudez J, Dávila-Sánchez A, Buvinic S, et al. Biological, mechanical and adhesive properties of universal adhesives containing zinc and copper nanoparticles. J Dent., 2019;82:45–55.
  80. Roig-Soriano X, Souto EB, Elmsmari F, Garcia ML, Espina M, Duran-Sindreu F, Sánchez-López E, González Sánchez JA. Nanoparticles in Endodontics Disinfection: State of the Art. Pharmaceutics., 2022;14(7):1519.
  81. Mutoh N, Tani-Ishii N. A biocompatible model for evaluation of the responses of rat periapical tissue to a new zinc oxide-eugenol sealer. Dent Mater J., 2011;30(2):176–82.
  82. Poggio C, Lombardini M, Colombo M, Dagna A, Saino E, Arciola CR, et al. Antibacterial effects of six endodontic sealers. Int J Artif Organs., 2011;34(9):908–13.
  83. Kozuszko SN, Sanchez MA, de Ferro MI, Sfer AM, Madrid AP, Takabatake K, Nakano K, Nagatsuka H, Rodriguez AP. Antibacterial activity and biocompatibility of zinc oxide and graphite particles as endodontic materials. J Hard Tissue Biol., 2017;26(4):311-8.
  84. Nicolai P, Mensi M, Marsili F, Piccioni M, Salgarello S, Gilberti E, et al. Maxillary fungus ball: zinc-oxide endodontic materials as a risk factor. Acta Otorhinolaryngol Ital., 2015;35(2):93–6.
  85. Rahman EF, Christiono S. Effectivity antibacterial zinc oxide eugenol with zinc oxide propolis for endodontic treatment in primary teeth. Odonto: Dental Journal., 2019;6(2):113-7.
  86. Shayani Rad M, Kompany A, Khorsand Zak A, Javidi M, Mortazavi SM. Microleakage and antibacterial properties of ZnO and ZnO: Ag nanopowders prepared via a sol–gel method for endodontic sealer application. J Nanopart Res., 2013;15:1-8.
  87. Aguiar AS, Guerreiro-Tanomaru JM, Faria G, Leonardo RT, Tanomaru-Filho M. Antimicrobial Activity and pH of Calcium Hydroxide and Zinc Oxide Nanoparticles Intracanal Medication and Association with Chlorhexidine. J Contemp Dent Pract., 2015;16(8):624–9.
  88. Alves MJ, Grenho L, Lopes C, Borges J, Vaz F, Vaz IP, et al. Antibacterial effect and biocompatibility of a novel nanostructured ZnO-coated gutta-percha cone for improved endodontic treatment. Mater Sci Eng C Mater Biol Appl., 2018;92:840–8.
  89. Ryu JH, Mangal U, Yoo J, Youm JH, Kim JY, Seo JY, Kim D, Kwon JS, Choi SH. Low concentration zinc oxide nanoparticles enrichment enhances bacterial and pro-inflammatory resistance of calcium silicate-based cements. J Mech Behav Biomed Mater., 2024;151:106399.
  90. Turssi CP, Vianna LMFF, Hara AT, do Amaral FLB, França FMG, Basting RT. Counteractive effect of antacid suspensions on intrinsic dental erosion. Eur J Oral Sci., 2012;120(4):349–52.
  91. Featherstone JDB. The caries balance: the basis for caries management by risk assessment. Oral Health Prev Dent., 2004;2 Suppl 1:259–64.
  92. Robinson C. Fluoride and the caries lesion: interactions and mechanism of action. Eur Arch Paediatr Dent., 2009;10(3):136–40.
  93. Staiger MP, Pietak AM, Huadmai J, Dias G. Magnesium and its alloys as orthopedic biomaterials: a review. Biomaterials., 2006;27(9):1728–34.
  94. Jawed M, Alabdulmonem W, Alkhamiss A, Alghsham R, Alsaeed T, Alhumaydhi F, Hershan A, Shahid S. Role of serum magnesium in dental caries. Bahrain Med Bull., 2021;43:327-30.
  95. Noori AJ, Kareem FA. The effect of magnesium oxide nanoparticles on the antibacterial and antibiofilm properties of glass-ionomer cement. Heliyon., 2019;5(10):e02568.
  96. 96.    MacKeown JM, Cleaton‐Jones PE, Fatti P. Caries and micronutrient intake among urban South African children: a cohort study. Community Dent Oral Epidemiol., 2003;31(3):213–20.
  97. Jawed M, Shahid SM, Qader SA, Azhar A. Dental caries in diabetes mellitus: role of salivary flow rate and minerals. J Diabetes Complications., 2011;25(3):183–6.
  98. Cheng L, Weir MD, Xu HH, Kraigsley AM, Lin NJ, Lin-Gibson S, Zhou X. Antibacterial and physical properties of calcium-phosphate and calcium-fluoride nanocomposites with chlorhexidine. Dent Mater., 2012;28(5):573–83.
  99. Salman SA, Usami T, Kuroda K, Okido M. Synthesis and characterization of cobalt nanoparticles using hydrazine and citric acid. J Nanotechnol., 2014;2014:1–7.
  100. Alkheraif AA, AlMufareh NA, AlQhtani FA, Asiri W, Abuhadi RI, Hamoud M, et al. Minocycline incorporated cobalt oxide nanoparticles in dental sealants: an in vitro study. Microsc Res Tech., 2022;85(7):2558–66.
Share Button
(Visited 138 times, 5 visits today)

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.